Bifunctional bamboo-like CoSe 2 arrays for high-performance asymmetric supercapacitor and electrocatalytic oxygen evolution

Bifunctional bamboo-like CoSe 2 arrays are synthesized by thermal annealing of Co(CO 3 ) 0.5 OH grown on carbon cloth in Se atmosphere. The CoSe 2 arrays obtained have excellent electrical conductivity, larger electrochemical active surface areas, and can directly serve as a binder-free electrode for supercapacitors and the oxygen evolution reaction (OER). When tested as a supercapacitor electrode, the CoSe 2 delivers a higher specific capacitance (544.6 F g −1 at current density of 1 mA cm −2 ) compared with CoO (308.2 F g −1 ) or Co 3 O 4 (201.4 F g −1 ). In addition, the CoSe 2 electrode possesses excellent cycling stability. An asymmetric supercapacitor (ASC) is also assembled based on bamboo-like CoSe 2 as a positive electrode and active carbon as a negative electrode in a 3.0 M KOH aqueous electrolyte. Owing to the unique stucture and good electrochemical performance of bamboo-like CoSe 2 , the as-assembled ACS can achieve a maximum operating voltage window of 1.7 V, a high energy density of 20.2 Wh kg −1 at a power density of 144.1 W kg −1 , and an outstanding cyclic stability. As the catalyst for the OER, the CoSe 2 exhibits a lower potential of 1.55 V (versus RHE) at current density of 10 mA cm −2 , a smaller Tafel slope of 62.5 mV dec −1 and an also outstanding stability.