Morphotropic phase boundary and electrical properties in (1−x)Bi0.5Na0.5TiO3−xBi(Zn0.5Ti0.5)O3 lead-free piezoceramics

( 1 − x ) Bi 0.5 Na 0.5 TiO 3 − x Bi ( Zn 0.5 Ti 0.5 ) O 3 [(1−x)BNT−xBZT, x=0, 0.025, 0.0375, 0.050, and 0.075] lead-free piezoceramics were prepared and their structures and electrical properties were investigated. It is found that BZT can increase the Curie temperature of BNT. A morphotropic phase boundary (MPB) separating rhombohedral and tetragonal phases exists near x=0.0375. As the result, the MPB composition shows improved electrical properties; the saturated polarization, remnant polarization, and coercive field are 42.0 μC/cm2, 36.5 μC/cm2, and 3.5 kV/mm, respectively, while the piezoelectric coefficient, planar electromechanical coupling factor, and unipolar strain are 92 pC/N, 0.22, and 0.08%, respectively. The structures and electrical properties are discussed by comparing with that of other BNT-based piezoceramics. Our results do not only supplement for BNT-based lead-free piezoceramics, but also may provide a way to develop new lead-free piezoceramics with high Curie temperature.