Poly(butylene terephthalate)/Poly(ethylene‐co‐alkyl‐acrylate)/carbon black (PBT‐EXA‐CB) blends, prepared through extrusion, were characterized as electrical conductive materials. In the composition range studied (55 ≤ PET % ≤ 75 w/w 5.5 ≤ CB % ≤ 11.1 w/w), various conductive behaviors were observed depending mainly on composition and poly(olefin) crystallinity. The observed positive temperature coefficient (PTC) is quite small compared to poly(olefin)‐CB systems, and our blends do not present a negative temperature coefficient (NTC) on complete melting of the CB‐containing phase, thus offering new possibilities for a regular electric power control. Volume expansion of both PBT and EXA was postulated to be the main parameter responsible for the thermal resistivity evolution through the range +20 to +170°C. A double‐percolation system between both the co‐continuous polymer phases and CB‐particles included in the poly(olefin) phase is postulated to explain these results.
No takes yet. Share an insight, caveat, or question.
Lagrève et al. (2001) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: