Poly(lactic acid)/poly(3‐hexylthiophene) composite nanofiber fabrication for electronic applications

Fibers of the biopolymer poly(lactic acid) (PLA) and the p‐type semiconducting polymer poly(3‐hexylthiophene) (P3HT) were fabricated using the electrospinning technique at low PLA concentration (5 wt%) in CHCl3. The fibers were several millimeters long and had diameters in the range 100 nm–4 µm. Nanofibers containing 63%/37% of PLA/P3HT were electroactive, and therefore were used to construct p–n diodes whose ideality parameter was 2.4 and rectification (on/off) ratio was 400 at ±1 V. These diodes were also able to sense UV radiation and remain operable with an increase in the on/off ratio and a lowering of the turn‐on voltage. By fabricating reusable and low‐cost multifunctional diodes from PLA/P3HT, the applications of PLA as a biocompatible and biodegradable polyester are expanded to include electronic device fabrication with low environmental impact.