Structure and properties of NR/BR blend/clay nanocomposites prepared by the latex method

Rubber blend/clay nanocomposites based on the 50/50 (wt %) natural rubber/butadiene rubber was prepared by the latex method via mixing the latex of 50/50 NR/BR blend with different amounts of the aqueous sodium montmorillonite (Na-MMT) dispersion and co-coagulating the mixture. XRD and TEM were used to characterize structure of the nanocomposites. It was found that fully exfoliated structure could be obtained by this method only when the low loading of layered silicate (up to 5 phr) is used. With increasing the clay content, both non-exfoliated (stacked layers) and exfoliated structures can be observed simultaneously in the nanocomposites. Nanocomposites showed mechanical properties better than the clay-free volcanizate. Moreover, modulus, tensile strength, elongation at break and tear strength increased significantly by increasing the clay amount up to 5 phr and then remained almost constant by further increasing the clay content. Improvement in the mechanical properties by increasing the clay loading up to 5 phr was attributed to the nano-reinforcement effect of Na-MMT. TGA results indicated an improvement in the main decomposition temperature by increasing the clay amount.