Improvement of dual-leached polycaprolactone porous scaffolds by incorporating with hydroxyapatite for bone tissue regeneration

Polycaprolactone (PCL)/hydroxyapatite (HA) composite scaffolds were prepared by combining solvent casting and salt particulate leaching with a polymer leaching technique. The hydrophilicity of the dual-leached scaffold was improved by alkaline (NaOH) treatment. Well-defined interconnected pores were detected by scanning electron microscopy. The water absorption capacity of the NaOH-treated PCL/HA dual-leached scaffold increased greatly, confirming that the hydrophilicity of the scaffold was improved by NaOH treatment. The compressive modulus of the PCL/HA dual-leached scaffold was greatly increased by the addition of HA particles. An indirect evaluation of the cytotoxicity of all PCL dual-leached scaffolds with mouse fibroblastic cells (L929) and mouse calvaria-derived pre-osteoblastic cells (MC3T3-E1) indicated that the PCL dual-leached scaffolds are non-toxic to cells. The ability of the scaffolds to support mouse calvaria-derived pre-osteoblastic cell (MC3T3-E1) attachment, proliferation, differentiation, and mineralization was also evaluated. Although the viability of cells was lower on the PCL/HA dual-leached scaffold than on the tissue-culture polystyrene plates (TCPS) and on the other substrates at early time points, both the PCL and NaOH-treated PCL/HA dual-leached scaffolds supported the attachment of MC3T3-E1 at significantly higher levels than TCPS. During the proliferation period (days 1-3), all of the PCL dual-leached scaffolds were able to support the proliferation of MC3T3-E1 at higher levels than the TCPS; in addition, the cells grown on NaOH-treated PCL/HA dual-leached scaffolds proliferated more rapidly. The cells cultured on the surfaces of NaOH-treated PCL/HA dual-leached scaffolds had the highest rate of mineral deposition.