High modulus semi‐crystalline polymers by solid state rolling

Solid state rolling of semi‐crystalline polymers is shown to be an effective method of producing high strength, high modulus tape at acceptable production rates. High density polyethylene tape was produced having a tensile strength exceeding 300 MPa and a tensile modulus of 8.7 GPa at production rates exceeding 8 m/min. A significant factor in producing highly oriented tape by the rolling process is roll temperature. Increasing the roll temperature from 25°C to 125°C not only increases the maximum extent of orientation achievable, but increases the mechanical properties at a given degree of thickness reduction. Internal frictional heat development limited the maximum thickness reduction ratio of polypropylene to 6.6:1. This reduction was reached by rolling at 150°C. The resultant tape had a tensile modulus of 5.1 GPa and a tensile strength of 300 MPa.