Enhanced thermal stability and flame resistance of polyurethane‐imide foams by adding silicon carbide

Polyurethane‐imide (PUI) foams containing both polyimide and polyurethane segments combined the advantage of fine mechanical properties as well as high thermal stability of the two polymers. To further improve the thermal stability and flame resistance ofPUIfoams, a series ofPUIcomposite foams with different content of SiC (silicon carbide) as fillers were prepared. The cell structure, mechanical properties, flame resistance, and thermal properties of resultingPUI/SiC composite foams were characterized in detail. The experimental results showed that the cell size distribution became uneven, the apparent density was increased, and the compressive strength decreased with the increase in silicon carbide content. Meanwhile, the limiting oxygen index (LOI) showed an increase from 24.7% to 28.1% with increasing of SiC content from 0% to 9.6%. The thermogravimetric analysis showed that the addition of SiC could significantly enhance the thermal stability and flame retardancy ofPUIfoams.