Three different low-temperature plasma-based methods for hydrophilicity improvement of polyethylene films at atmospheric pressure

Three different low-temperature plasma-based methods were used to improve the surface hydrophilicity of polyethylene (PE) films, and all the modification processes were carried out by employing an atmospheric pressure plasma jet (APPJ) system. (a) PE films were directly modified by APPJ using a gas mixture of He and O 2 . (b) Acrylic acid (AA) was introduced into the system and a polymer acrylic acid (PAA) coating was deposited onto the PE films. (c) AA was grafted onto the PE surface activated by plasma pre-treatment. It was found that the hydrophilicity of the PE films was significantly improved for all the three methods. However, the samples modified by Process (a) showed hydrophobicity recovery after a storage time of 20 days while no significant change was found in samples modified by Process (b) and Process (c). The Fourier transform infrared spectroscopy (FTIR) results indicated that the most intensive C=O peak was detected on the PE surface modified by Process (c). According to the X-ray photoelectron spectroscopy (XPS) analysis, the ratios of oxygen-containing polar groups for samples modified by Process (b) and Process (c) were higher than that modified by Process (a).