Aliphatic polycarbonate‐based polyurethane elastomers and nanocomposites. I. The influence of hard‐segment content and macrodiol‐constitution on bottom‐up self‐assembly

Aliphatic polycarbonate‐based polyurethane (PC‐PU) elastomers as well as their nanocomposites with organic‐modified clay (bentonite for organic system) were synthesized. Macrodiols (MD) (randomly copolymerized aliphatic PC‐glycols of molecular weight of about 2000: T5652, T4672, and T4692), hexamethylene diisocyanate, and butane‐1,4‐diol were used as starting materials. Solid‐state NMR and Fourier transform infrared spectroscopy, small‐angle X‐ray scattering, wide‐angle X‐ray diffraction, atomic force microscopy, and transmission electron microscopy were used for studying the bottom‐up self‐assembly of building units from the segmental level up that of organized structures of micrometer sizes. Contents of hard segments formed by the reaction of chain extender with diisocyanate plays a dominant role for the degree of ordering and related phenomena, while the MD chain has only limited effect on PC‐PU properties. The spectroscopy and scattering experiments suggest that bentonite particles incorporate well in the structure and promote the ordering of hard segment domains in PC‐PU matrix as compared with the nanofiller‐free analogue.