Crystallization and Properties of Fe 2 O 3 —CaO—SiO 2 Glasses

Nucleation and crystal growth rates and properties were studied in a two‐stage heat treatment process for Fe 2 O 3 ‐CaO‐SiO 2 glasses. Glass transition (T g ) and crystallization temperatures (T c ) for the glasses lay between about 612.0° and 710.0°C, and 858.5° and 905.0°C, respectively, and magnetite was the main crystal phase. For a glass of 40Fe 2 O 3 . 20CaO·40SiO 2 (in wt%) the maximum nucleation rate was (68.6 ± 7) × 10 6 /mm 3 ·s at 700°C, and the maximum crystal growth rate was 9.0 nm/min 1/2 at 1000°C. The mean crystal size of the magnetite increased from 30 to 140 nm with variation of nucleation and crystal growth conditions. The glass showed the maxima in saturation magnetization and coercive force, 212.1 × Wb/m 2 and 30.8 × 10 3 A/m, when heat‐treated for 4 h at 1000°C and 1050°C, respectively. The variation of the saturation magnetization could be quantitatively interpreted well in terms of the volume fraction of the magnetite, whereas that of the coercive forces could be explained only qualitatively in terms of the particle size of the magnetite. Hysteresis losses showed the maximum value of 1493 W/m 3 when heat‐treated at 1000°C for 4 h prenucleated at 700°C for 60 min, and increased linearly with increasing heat treatment time under a magnetic field up to 800 × 10 3 A/m.