The microstructures and dielectric properties of barium strontium titanate glass–ceramics are closely related to the AlF 3 and MnO 2 additions. The grain morphology was changed by adding AlF 3 , while the dielectric loss was decreased significantly by adding MnO 2 . At the same time the breakdown strength (BDS) was improved by doping 4 mol% AlF 3 and 1 mol% MnO 2 with the glass–ceramics. The present investigation resulted in the development of glass–ceramic compositions with high dielectric BDS and low dielectric loss for high energy density capacitor applications.