The present work reviews previous research on the evolution of porosity. It presents new results from a detailed study on the evolution of porosity during casting, heat treatment and creep of a single crystal Ni-base superalloy subjected to uniaxial tensile creep at 1050 °C and 160 MPa in [001] and [110] directions. A quantitative metallographic study was performed on carefully polished metallographic cross sections, monitoring sampling fields of 4500 × 1000 µm2 using the back scatter contrast of an analytical scanning electron microscope; evolutions of pore sizes and pore form factors were analyzed and all important details which were previously revealed in a synchrotron study could be reproduced. In addition, it was observed that micro cracks form at larger cast pores. They interlink and thus initiate final rupture. The [110] tensile creep tests showed lower rupture strains than the [001] experiments. In agreement with earlier work, this can be rationalized on the basis of aligned porosity along primary dendrites.
No takes yet. Share an insight, caveat, or question.
Buck et al. (2015) studied this question.
Synapse has enriched 5 related papers. Consider them for comparative context: