Polyelectrolyte‐grafted carbon nanotubes: Synthesis, reversible phase‐transition behavior, and tribological properties as lubricant additives

A novel polyelectrolyte‐grafted multiwalled carbon nanotubes (MWCNTs‐g‐PILs) which possesses a hard backbone of MWCNTs and a soft shell of brush‐like poly (ionic liquids) (PILs) has been synthesized via the surface atom transfer radical polymerization (ATRP). Chemical structure and the grafted PILs quantities of MWCNTs‐g‐PILs were determined by FTIR, TGA, and XPS. TEM and FE‐SEM observations indicate that the nanotubes were coated with a PILs layer, exhibiting core‐shell nanostructures with the PILs chains as the brush‐like or hairy shell and the MWCNTs as the hard backbone. Furthermore, the effect of counter‐anions on the solubility of MWCNTs‐g‐PILs was investigated. The results indicate that relative solubility of MWCNTs‐g‐PILs in various solvents could be switched by anion exchange. This tunable solubility results in the formation of the cycle of reversible phase‐transition. Tribological property of MWCNTs‐g‐PILs as additives in base lubricant 1‐methyl‐3‐butylimidaaolium hexafluorophosphate (LP104) was evaluated using an Optimol SRV oscillating friction and wear tester, confirming that MWCNTs‐g‐PILs are the excellent antiwear and friction‐reducing additives, which can amend the tribological properties of base lubricant significantly. This is attributed to the good dispersibility and core‐shell structure of MWCNTs‐g‐PILs. These results reported in this work may open primarily toward constructing a bridge among carbon nanotues (CNTs), ILs, and lubricant additives and secondarily to prove that CNTs (modified CNTs) as lubricant additives are promising candidates.