Particle formation in interval III of the emulsion polymerization of styrene with aerosol‐MA as an emulsifier

Particle nucleation in the seeded emulsion polymerization of styrene in the presence of Aerosol‐MA emulsifier micelles and in the absence of monomer droplets (interval III) was investigated. The seed particles were swollen with different amounts of the styrene monomer before the experiments. A larger number of polymer particles formed in interval III than in the corresponding seeded batch operation in the presence of monomer droplets. The increase in the number of particles could be attributed to the reduced rate of growth of new particles, which retarded the depletion of emulsifier micelles. The number of secondary particles initially increased with the initial polymer weight ratio in the seed particles (wp0) but decreased at a higher range of wp0, after reaching a maximum at wp0 = 0.60, and eventually was reduced to zero. At high values of wp0 (>0.75), polymerization occurred in the seed particles, whereas few or no new particles were formed despite the presence of micelles. The cessation of particle formation at high conversions was ascertained with a semibatch process in which the neat monomer feed was added to the reaction vessel containing the seed particles and emulsifier micelles. For wp0 > 0.85, the emulsifier micelles were disintegrated to stabilize the seed particles with no secondary particle formation. The possible reasons for the cessation of particle formation at high wp0 were examined. The size distribution of secondary particles showed a positive skewness in terms of volume because of the declining rate of growth for particles, together with a low rate of growth for small particles. The distribution breadth of new particles sharpened with increasing wp0.