Response Characteristics of Thermoresponsive Polymers Using Nanomechanical Cantilever Sensors

We investigated coatings of thermally responsive thin polymer films prepared on nanomechanical cantilever sensor (NCS): (i) a PNIPAM brush, and (ii) an interlinked ppDEA polymer. Upon heating from 22 to 50 °C in water, a minimum in the differential deflection between 31.9 ± 1.7 °C (PNIPAM) and 47.7 ± 1.9 °C (ppDEA) was measured. The minimum in differential deflection can be associated with the lower critical solution temperature (LCST) of the films. Below the LCST the NCS deflection corresponds to a bending toward the thermally responsive polymer film side, associated to dehydration. At higher temperature, the deflection was reversed, i.e., away from the polymer coating. This response is mainly attributed to a bimaterial effect between the collapsed polymer and the NCS material. The LCST of the PNIPAM brush layer and the ppDEA film were close to that reported for the bulk polymers. magnified image