Tribological investigation of diamond nanoparticles for steel/steel contacts in boundary lubrication regime

This paper presents an investigation of nanodiamond additives (ND) in combination with copper oxide (CuO) and hexagonal boron nitride (h-BN) particles mixed in PAO (poly-alpha-olefin) oil. The experimentation was performed for a ball on disc configuration using steel/steel contacts in the boundary lubrication regime. The loads were varied from 20 to 100 N and sliding velocity was kept constant at 0.58 m/s. The wear behavior was evaluated using SEM images of the worn-out disc surfaces. EDS analysis of the samples was performed to find out the chemical content of the worn surfaces. Results obtained therein demonstrated that oil containing CuO/ND and h-BN/ND exhibited better frictional and wear characteristics. For CuO/ND containing lubricant, the maximum decrease in friction coefficient is 15.45% in comparison to the CuO oil, whereas for h-BN/ND containing additives the overall decrease is 25.45%. It was observed that the combined effect of CuO/ND and h-BN/ND due to their intrinsic characteristics led to the overall improvement in lubrication properties of the base oil.