Origin of Texture Development in Barium Bismuth Titanate Prepared by the Templated Grain Growth Method

Microstructure development was examined for BaBi 4 Ti 4 O 15 prepared by the templated grain growth method, and the origin of texture development was discussed. The microstructure development in a compact composed of a platelike template and equiaxed matrix grains was characterized as follows: (1) the template grains thickened at an early stage; (2) the matrix grains changed their shape from equiaxed to platelike, and simultaneously, the plate faces aligned parallel to those of template grains; and (3) a group of large grains with mutually parallel alignment was formed by prolonged heating at high temperature. Texture developed during these microstructural changes, and process (2) made the greatest contribution toward texture development.