In this article, PA6/poly(tetrafluoroethylene) (PTFE) composites were prepared by internal mixer with high rotor speed. The existence of PTFE nano‐fibrillation network structure was observed by scanning electron microscopy (SEM) analysis. The effect of PTFE on crystallization and rheological behavior of PA6 was evaluated. The result showed that the PTFE fibrils improved the crystallization properties of PA6 and do not change the crystal structure. The PTFE effectively enhanced the melt strength of PA6 by fibrillation. The PA6/PTFE composites were then foamed assisted by supercritical CO2. The PTFE was used as cell nucleating agent, crystal nucleating agent and melt strength enhancement agent in the foaming process. Finally, the microcellular PA6 foams were successfully obtained with the cell density higher than 109 cells/cm3, the cell size of ca. 14 μm and the volume expansion ratio of 16.
No takes yet. Share an insight, caveat, or question.
Han et al. (2021) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: