Critical Current Properties in REBa₂ Cu₃Oy Films With Nanorods Depending on Growth Conditions

Growth temperature (Ts) dependent microstructures of nanorods were clarified for BaNb2O6(BNO)-doped YBa2Cu3Oy(Y123) films. The morphology of BNO in the Y123 matrix was changed from fluctuated nanorods to uniform nanorods with the increase inTs. Reflecting this change in the nanorod morphology, spatial distribution of local critical current density (Jcl) determined from the percolation transition model became sharp with the increase inTs. The sharp distribution ofJclled to a steep slope of electric field vs. current density curve and a sharpJcpeak underB//cin the magnetic field angular dependence. The evaluation of the distribution ofJclis a strong tool to understand quantitatively the relationship between the microstructure of nanorods and critical current properties for RE123 films with nanorods. To optimize the critical current properties under the magnetic field for RE123 coated conductors with nanorods, precise control ofTsis very important in the production process.