Piezoresistive gauge factor of hydrogenated amorphous carbon films

In this paper we report on the transport properties of hydrogenated amorphous carbon (a-C:H) which is an attractive material for strain gauges and can also be used in flow meters, accelerometers and vibrational sensors. The a-C:H films were deposited at −350 V bias voltage on silicon (Si) substrates using plasma assisted chemical vapor deposition (PACVD). Current–voltage characteristics of a-C:H/ n -Si heterojunctions show ohmic behavior within operating voltages of ±1 V. In the higher voltage range the Frenkel–Poole mechanism is dominant. Conduction is thermally activated at temperatures ranging from 23 °C to 150 °C. The activation energy amounts to 0.48 eV. A-C:H resistors are successfully integrated as strain gauges in Si bulk micromachined force sensors. Piezoresistive gauge factors are measured for the a-C:H strain gauge resistors in the temperature range 23–60 °C. The measured piezoresistive gauge factors are in between 40 and 90 for a-C:H with resistivities in the range 100–700 MΩ cm.