Microstructure and precipitation in Al–Li–Cu–Mg–(Mn, Zr) alloys

Hot rolled Al–6Li–1Cu–1Mg–0·2Mn (at.-%) (Al–1·6Li–2·2Cu–0·9Mg–0·4Mn, wt-%) and Al–6Li–1Cu–1Mg–0·03Zr (at.-%) (Al–1·6Li–2·3Cu–1Mg–0·1Zr, wt-%) alloys developed for age forming were studied by tensile testing, electron backscatter diffraction (EBSD), three-dimensional atom probe (3DAP), transmission electron microscopy (TEM) and differential scanning calorimetry (DSC). For both alloys, DSC analysis shows that ageing at 150°C leads initially to formation of zones/clusters, which are later gradually replaced by S phase. On ageing at 190°C, S phase formation is completed within 12 h. The precipitates identified by 3DAP and TEM can be classified into (a) Li rich clusters containing Cu and Mg, (b) a plate shaped metastable precipitate (similar to GPB2 zones/S″), (c) S phase and (d) δ′ spherical particles rich in Li. The Zr containing alloy also contains β′ (Al3Zr) precipitates and composite β′/δ′ particles. The β′ precipitates reduce recrystallisation and grain growth leading to fine grains and subgrains.