Identification of Intrinsic ab-Plane Pinning in rm YBa₂rm Cu₃rm O₇ Thin Films and Coated Conductors

The angular-dependent critical current density J/sub c/ in YBa/sub 2/Cu/sub 3/O/sub 7/ films grown by pulsed laser deposition exhibit a sharp peak for magnetic field orientations near the ab plane, which arises from the combined effects of intrinsic pinning and extended defects parallel to the planes. An analysis of the temperature and field dependence of the height and width of this peak allows us to distinguish both contributions. We find that, in a film on single crystal substrate, the peak at low fields is due primarily to the extended defects, but at high fields it is dominated by intrinsic pinning. We compare these results with those of coated conductors with a larger density of ab-oriented correlated defects. We show a novel effect consisting in an inverse correlation between J/sub c/ and the power law exponent (N) of the I-V curves that only occurs in the intrinsic-pinning dominated regime, and we present an interpretation of its origin.