Ga vacancies as dominant intrinsic acceptors in GaN grown by hydride vapor phase epitaxy

Positron annihilation measurements show that negative Ga vacancies are the dominant acceptors in n-type gallium nitride grown by hydride vapor phase epitaxy. The concentration of Ga vacancies decreases, from more than 1019 to below 1016 cm−3, as the distance from the interface region increases from 1 to 300 μm. These concentrations are the same as the total acceptor densities determined in Hall experiments. The depth profile of O is similar to that of VGa, suggesting that the Ga vacancies are complexed with the oxygen impurities.