EXAFS studies of rare-earth metaphosphate glasses

An extended x-ray-absorption fine structure (EXAFS) study has been carried out on a range of rare-earth metaphosphate R(PO₃)₃ glasses of growing interest in optical communications and laser technologies. Phosphate glasses modified using the rare-earth oxides Pr₆{O}₁₁$, ${Nd}₂O₃, Eu₂{O}₃$, ${Gd}₂O₃, Tb₂{O}₃$, and ${Ho}₂O₃, have been investigated using their respective rare-earth LIII absorption edges. The data provide information on the local environment of the rare-earth ion within the phosphate glass matrix constructed from linked PO₄ tetrahedra. The rare-earth ions occupy sites with an average coordination number in the range, $6<~N<~8$, the surrounding atoms being oxygen. The first shell interatomic distance over the range of rare-earth ions establishes the rare-earth contraction of ionic radii with increasing atomic number in a series of glasses. There is also evidence for a rare-earth-phosphorus correlation between 2.7 and 3.6 {}, and a further rare-earth-oxygen correlation at approximately 4 {}. The EXAFS spectrum shows no evidence for R-R correlations within the short-range order, a result especially pertinent to the optical and magnetic properties of the glasses. The fractal dimensionality 4C₁₁/B of these glasses, obtained from the elastic stiffnesses determined from ultrasonic wave velocities, ranges between 2.3 and 2.8, indicating that their connectivity tends towards having a three-dimensional character.