Dry sliding behavior of aluminum alloy 8011 with 12% fly ash composites

This research focused on the fabrication of aluminum alloy 8011 with 12% fly ash (FA) composite (AA8011%–12% FA) using the stir casting method. A three-level central composite design experiment was developed using response surface methodology with various parameters such as load, time, and sliding velocity varied in the range of 5 to 15 N, 5 to 15 min, and 1.5 to 4.5 m.s−1, respectively. Dry sliding wear tests were performed as per the experimental design using a pin on disc at room temperature. The obtained regression result indicated that the developed model performed well in relating the wear process parameters and predicted the wear behavior of the composite. The surface plot showed that the wear rate increases with increase in load, time, and sliding velocity. Hardness was evaluated by Vickers hardness testing machine. Moreover, the surface morphology of the worn-out composite was examined using a scanning electron microscope.