Origin of the Ultrafast Response of the Lateral Photovoltaic Effect in Amorphous MoS 2 /Si Junctions

The lateral photovoltaic (LPV) effect has attracted much attention for a long time because of its application in position-sensitive detectors (PSD). Here, we report the ultrafast response of the LPV in amorphous MoS 2 /Si (a-MoS 2 /Si) junctions prepared by the pulsed laser deposition (PLD) technique. Different orientations of the built-in field and the breakover voltages are observed for a-MoS 2 films deposited on p- and n- type Si wafers, resulting in the induction of positive and negative voltages in the a-MoS 2 / n -Si and a-MoS 2 / p -Si junctions upon laser illumination, respectively. The dependence of the LPV on the position of the illumination shows very high sensitivity (183 mV mm –1 ) and good linearity. The optical relaxation time of LPV with a positive voltage was about 5.8 μs in a-MoS 2 / n -Si junction, whereas the optical relaxation time of LPV with a negative voltage was about 2.1 μs in a-MoS 2 / p -Si junction. Our results clearly suggested that the inversion layer at the a-MoS 2 /Si interface made a good contribution to the ultrafast response of the LPV in a-MoS 2 /Si junctions. The large positional sensitivity and ultrafast relaxation of LPV may promise the a-MoS 2 /Si junction’s applications in fast position-sensitive detectors.