Mechanical and Morphological Properties of Polypropylene and Regenerated Tire-Rubber Blends

Mechanical properties and morphology of blends prepared from polypropylene (PP) and 5–20 wt% of regenerated tire-rubber (RgR) were studied. The samples were prepared in a twin-screw extruder. The addition of maleic anhydride-functionalized polypropylene (PP-g-MAH) was also investigated. Tensile and flexural moduli, tensile strength at break, elongation at break and Izod impact resistance at 23°C were increased by the addition of 15 wt% of regenerated rubber and 5 wt% of PP-g-MAH. Atomic force microscopy (AFM) and scanning electron microscopy (SEM) analyses showed some interaction between PP and RgR and considerable modification of the compatibilized mixture morphology. The fracture surface of the blend with PP-g-MAH showed a better interaction between the PP matrix and the regenerated rubber domains, for all blends. Well-dispersed particles of the rubber in the polypropylene matrix were observed. DSC showed that PP crystallizes on cooling at lower temperatures as the RgR content increases. The decrease in crystallization temperature is more evident for blends with 5 wt% PP-g-MAH.