Effects of carbon nanotubes on dynamic mechanical property, thermal property, and crystal structure of poly( L ‐lactic acid)

Effects of carbon nanotubes (CNT) on the dynamic mechanical property, thermal property, and crystal structure of poly(L‐lactic acid) (PLLA) were investigated. Dynamic mechanical analysis (DMA) found that CNT via grafting modification with PLLA (CNT‐g‐PLLA) could result in effective reinforcing effects. Tan δ of DMA found that CNT‐g‐PLLA was compatible with the PLLA matrix, giving a single Tg of the composite with a higher CNT‐g‐PLLA loading giving a higher Tg of the composite. Wide angle X‐ray diffraction (WAXD) data demonstrated that CNT could assist the disorder‐to‐order (α′‐to‐α) transition in PLLA crystals but did not lead to a more compact chain packing of the crystal lattice in PLLA composites than in pure PLLA. The equilibrium melting temperature (T ) obtained from Hoffman‐Weeks plots were found to increase with increasing CNT‐g‐PLLA content. Small angle X‐ray scattering data revealed that thicknesses of crystal layer and amorphous layer of PLLA both decreased with increasing CNT contents.