Polyphenylene Sulfide Ultrafine Fibrous Membrane Modified by Nanoscale ZIF-8 for Highly Effective Adsorption, Interception, and Recycling of Iodine Vapor

In this study, two novel composite membranes containing nanoscale ZIF-8 and polyphenylene sulfide (PPS) nonwoven fabric were prepared via hydrothermal (PPS-ZIF-8) and biomimetic mineralization (PPS-ZIF-8-BSA; BSA, bovine serum albumin) approaches. The biomimetic mineralization approach in particular was extremely rapid and mild, and crystalline ZIF-8 was coated on the PPS substrate in only a few seconds at room temperature. The maximum iodine adsorption capacities of the PPS-ZIF-8 and PPS-ZIF-8-BSA membranes were 2.51 and 2.07 g/g, respectively. The composite fibrous membranes were able to capture trace iodine vapor under differential pressures ranging from 0 to 1000 Pa without almost any iodine vapor leakage. The composite membranes can be applied in harsh environments because of the excellent stability of ZIF-8 and the PPS high-performance fibers. This study provides a promising strategy to fabricate novel adsorption materials for the collection of radioactive iodine during nuclear waste disposal.