Mechanical properties, thermal stability, and crystallization kinetics of poly(3‐hydroxybutyrate‐ co ‐4‐hydroxybutyrate)/calcium carbonate composites

Bacterial polyester poly(3‐hydroxybutyrate‐ co ‐4‐hydroxybutyrate) (P3/4HB) containing 5 mol% 4HB was composited with different calcium carbonate (CaCO 3 ) fillers. The effect of CaCO 3 contents on thermal properties, mechanical property, and crystallization kinetics was evaluated. The thermal stability of P3/4HB was reduced by mixing with CaCO 3 particles. With increasing CaCO 3 content, the elongation at break, tensile strength, and impact strength decrease; however, elastic modulus increases. When P3/4HB with 20 mol% 4HB was added into the P3/4HB/CaCO 3 composite, the impact strength were enhanced significantly; however, the elongation at break and tensile strength were only slight to moderate improvements. However, when compared with nano‐ and light‐CaCO 3 , heavy CaCO 3 had the best mechanical properties. The nonisothermal and isothermal crystallization results demonstrated that the crystallization rate of P3/4HB was reduced and the highest crystallinity was obtained for all kinds of CaCO 3 fillers at 40 phr content. POLYM. COMPOS., 2011.