The stress–life fatigue behaviour of aluminium alloy foams

The tension–tension and compression–compression nominal stress versus fatigue life responses of Alulight closed cell aluminium alloy foams have been measured for the compositions Al–1Mg–0.6Si and Al–1Mg–10Si (wt %), and for relative densities in the range 0.1–0.4. The fatigue strength of each foam increases with the relative density and with the mean applied stress, and is greater for the transverse orientation than for the longitudinal orientation. Under both tension–tension and compression–compression loading the dominant cyclic deformation mode appears to be material ratchetting; consequently, the fatigue life is highly sensitive to the magnitude of the applied stress. A micromechanical model is given to predict the dependence of life upon stress level and relative density. Panels containing a central hole were found to be notch insensitive for both tension–tension and compression–compression fatigue loading: the net‐section strength equals the unnotched strength.