Pressure‐Suppressed Carrier Trapping Leads to Enhanced Emission in Two‐Dimensional Perovskite (HA)2(GA)Pb2I7

A remarkable PL enhancement by 12 fold is achieved using pressure to modulate the structure of a recently developed 2D perovskite (HA)2(GA)Pb2I7 (HA=n‐hexylammonium, GA=guanidinium). This structure features a previously unattainable, extremely large cage. In situ structural, spectroscopic, and theoretical analyses reveal that lattice compression under a mild pressure within 1.6 GPa considerably suppresses the carrier trapping, leading to significantly enhanced emission. Further pressurization induces a non‐luminescent amorphous yellow phase, which is retained and exhibits a continuously increasing band gap during decompression. When the pressure is released to 1.5 GPa, emission can be triggered by above‐band gap laser irradiation, accompanied by a color change from yellow to orange. The obtained orange phase could be retained at ambient conditions and exhibits two‐fold higher PL emission compared with the pristine (HA)2(GA)Pb2I7.