Linear polyurethanes made from naturally occurring tartaric acid

Naturally occurring tartaric acid was used as raw material for the synthesis of novel linear polyurethanes (PURs) bearing two carboxylate side‐groups in the repeating unit. Aliphatic and aromatic PURs were obtained by reaction in solution of alkyl and benzyl tartrates with hexamethylene diisocyanate and 4,4′‐methylene‐bis(phenyl isocyanate), respectively. All the novel PURs were thermally stable and optically active. The aliphatic carboxylate‐containing PURs had Mw in the 40–70 kDa range, with PD between 2.1 and 2.5; all were semicrystalline polymers with melting temperatures between 100 and 150 °C and Tg in the 50–80 °C range. The aromatic PURs were amorphous materials with molecular weights between 18 kDa and 25 kDa and Tg above 130 °C. Hydrogenolysis of the PUR made from hexamethylene diisocyanate and benzyl tartrate yielded PURs containing up to 40% of free carboxylic side‐groups. The tartrate‐derived PURs displayed enhanced sensitivity to hydrolysis compared with their unsubstituted 2,6‐PUR homologs. The PURs bearing free carboxylic groups were unique in being degraded by water upon incubation under physiological conditions.