Effect of microstructure and strain on the degradation behavior of novel bioresorbable iron–manganese alloy implants

Advancing the understanding of microstructural effects and deformation on the degradability of Fe-Mn bioresorbable alloys (specifically, Fe-33%Mn) will help address the current problems associated with designing degradable fracture fixation implants for hard tissues. Potentiostatic polarization tests were conducted on a wide variety of metal samples to examine how different deformation processes affect the instantaneous rate of degradation of Fe-Mn alloys. Large-strain machining (LSM), a novel severe plastic deformation (SPD) technique was utilized during these experiments to modify the degradation properties of the proposed Fe-Mn alloy. It was discovered that Fe-33%Mn after LSM with a rake angle of 0° (effective strain = 2.85) showed the most promising increase in degradation rate compared to as-cast, annealed, and additional deformation conditions (rolled and other LSM parameters) for the same alloy. The mechanisms for enhancement of the corrosion rate are discussed.