Preparation of Zirconia Fibers via a Simple Aqueous Sol‐Gel Method

Polycrystalline tetragonal zirconia fiber was obtained by pyrolysis of precursor fibers from citrate‐acetate‐zirconium complex solution. The viscous zirconia sol with good spinnability was prepared by aging the starting solution of ZrOCl2 · 8H2O (ZOC) in the presence of acetic acid (HA) and citric acid (CA). The effects of molar ratio of zirconium cation to carboxylic acid and the aging time on the formation of spinnable sol were investigated. Thermogravimetric (TG) analysis, x‐ray diffraction (XRD), infrared (IR) spectra, and scanning electron microscope (SEM) techniques were used to characterize the sintered fibers. The results show that the fibers obtained at 1400°C are crack‐free with diameter of ca. 5–10 µm.