Thermoplastic polyamide elastomers were obtained by polymerization of aminobenzoyl‐substituted telechelics derived from poly(tetrahydrofuran)‐diols (number‐average molecular weight: 1400 or 2000 g mol−1) with several diacid dichlorides (terephthaloyl dichloride, 4,4′‐biphenyldicarbonyl dichloride, or 2,6‐naphthalenedicarbonyl dichloride) and chlorotrimethylsilane in N,N‐dimethylacetamide at 0–20 °C. The as‐prepared polymers had melting temperatures above 190 °C and exhibited elastic properties at room temperature, as evidenced by dynamic mechanical analysis and stress–strain measurements. The polymer with 2,6‐naphthalenedicarboxamide hard segments had the widest rubbery plateau within the series, the highest extension at break, and good recovery properties.