MgB 2 superconducting joints for persistent current operation

High-performance superconducting joints are essential for realizing persistent-mode magnets. Herein, we propose a concept and fabrication of such superconducting joints, which yielded reliable performance in the operating temperature range of 4.2–25 K. MgB 2 –MgB 2 joints in magnets are known to result in deterioration of localized electrical, thermal, and mechanical properties. To overcome these problems, the ends of the two wires are inserted into a pellet press, which is then filled with a mixture of unreacted magnesium and boron powders, followed by heat treatment. The critical current capacity and joint resistance were precisely evaluated by the standard four-probe method in open-circuit and by field-decay measurements in a closed-loop, respectively. These joints demonstrated up to 66% of the current-carrying capacity of unjoined wire at 20 K, 2 T and joint resistance of 1.4 × 10 −12 Ω at 4.2 K in self-field.