Synthesis of polyacetals with various main‐chain structures by the self‐polyaddition of vinyl ethers with a hydroxyl function

To establish the optimum conditions for obtaining high molecular weight polyacetals by the self‐polyaddition of vinyl ethers with a hydroxyl group, we performed the polymerization of 4‐hydroxybutyl vinyl ether (CH2CHOCH2CH2CH2CH2OH) with various acidic catalysts [p‐toluene sulfonic acid monohydrate, p‐toluene sulfonic anhydride (TSAA), pyridinium p‐toluene sulfonate, HCl, and BF3OEt2] in different solvents (tetrahydrofuran and toluene) at 0 °C. All the polymerizations proceeded exclusively via the polyaddition mechanism to give polyacetals of the structure [CH(CH3)OCH2CH2CH2CH2O]n quantitatively. The reaction with TSAA in tetrahydrofuran led to the highest molecular weight polymers (number‐average molecular weight = 110,000, weight‐average molecular weight/number‐average molecular weight = 1.59). 2‐Hydroxyethyl vinyl ether, diethylene glycol monovinyl ether, cyclohexane dimethanol monovinyl ether, and tricyclodecane dimethanol monovinyl ether were also employed as monomers, and polyacetals with various main‐chain structures were obtained. This structural variety of the main chain changed the glass‐transition temperature of the polyacetals from approximately −70 °C to room temperature. These polyacetals were thermally stable but exhibited smooth degradation with a treatment of aqueous acid to give the corresponding diol compounds in quantitative yields.