Dynamic mechanical and dielectric properties of epoxidized SBS triblock copolymer

The morphological and dynamic properties of epoxidized styrene–butadiene–styrene block copolymers were studied and compared with their parent styrene–butadiene–styrene block copolymer (SBS). Two peaks were observed in the mechanical loss (tan δ) curve which can be attributed to segmental motion of epoxidized polybutadiene (EPPB) and polystyrene. Analysis by DSC thermograms also showed the linear increase of glass transition temperature for EPPB domain with the epoxy group content. Phase separated structures of epoxidized SBS as observed by TEM suggests a considerable degree of mixing occurred between phases after 80 mol % of the double bonds in SBS were epoxidized. The interfacial region displays a third peak and causes much steeper drop in modulus at higher temperature than Tg of EPPB. Parallel dielectric relaxation measurements were also made in the frequency range of 30 Hz–1 KHz as a function of temperature. In each dielectric constant (ϵ′) curve, there is a maximum near the Tg of EPPB determined from the dielectric loss tangent curve. The shift in Tg of EPPB versus epoxy group content was consistent with that measured by the thermal and dynamic mechanic analysis. These findings indicated an 8°C shift in glass transition temperature as the epoxy group content in EPPB increased 10%.