Cross‐linked Multilayer Polymer‐Clay Nanocomposites and Permeability Properties

Electrostatically layered aluminosilicate nanocomposites have been prepared by the sequential deposition of poly(allylamine hydrochloride)/poly(acrylic acid)/poly(allylamine hydrochloride)/saponite (PAH/PAA/PAH/saponite)10 on poly(ethylene terephtalate) (PET) film. Exfoliated saponite nanoplatelets were obtained by extensive shaking, sonication, and centrifugation of a water suspension. To minimize permeability and improve the mechanical integrity, cross‐linking of composite films was carried out at different temperatures. The formation of amide linkage induced through heating was observed by Fourier Transform Infrared (FT‐IR) and x‐ray photoelectron spectroscopy (XPS). The cross‐linking of nanocomposites (PAH/PAA/PAH/saponite)10 showed 60% decrease in permeability of oxygen when compared with the pristine PET substrate film. In contrast, water permeability of the nanocomposite membrane was not affected by heating temperature and deposition cycles.