Mechanical degradation of semi‐dilute polymer solutions in laminar flows

Mechanical degradation of a semi‐dilute solution of non‐hydrolyzed polyacrylamide was studied under laminar flow conditions through fine capillary systems. Using a multi‐pass device and capillary tubes of the same diameter and of various lengths we have shown that mechanical degradation (i) occurs at a critical value of the wall shear rate, chosen as a reference deformation rate, which is slightly higher than that of the appearance of high pressure losses in the entrance region of the capillary tube; (ii) is independent of the capillary tube length; (iii) increases with the number of passes N up to a maximum value for a limiting number of passes Nlim which is a decreasing function of deformation rates but does not depend on capillary length. The amount of degradation is expressed in terms of loss of viscous dissipation in shear and transient elongational flow. This last point is determined by studying the total end pressure loss through the capillary tube as a function of the pass number. The high pressure loss is related to viscous dissipation on macromolecules stretched by rapid converging flow. A comparison between a fresh and a fully degraded solution indicates that the degradation affects shear viscosity much less than viscous dissipation in rapid converging flow which is related to the properties of extended macromolecules. Both experimental results and theoretical interpretation suggest that, in our capillary system, the mechanical degradation occurs in the entrance region of the capillary where macromolecules are stretched and consequently submitted to extensional forces which can overcome the C–C bonds strength.