Influence of nanoparticle size to the electrical properties of naphthalenediimide on single-walled carbon nanotube wiring

Nanoparticles of N,N'-bis(n-alkyl)tetracarbonatenaphthalenediimide (NDI) were adsorbed on single-walled carbon nanotube (SWNT) wires dispersed on a SiO(2) substrate. The electrical properties were measured along the long axis of the SWNTs, and in all cases through the nanoparticles showed rectification in semiconducting I-V curve. The plateau width of the I-V curve through the NDI nanoparticles on metallic SWNTs decreased as the particle size increased, while the rectification ratio increased. The conduction mechanism was changed from tunneling conduction to Schottky-like conduction and their boundary is at about 3 nm diameter.