Transition Metal Ion (Mn 2+ , Fe 2+ , Co 2+ , and Ni 2+ )-Doped Carbon Dots Synthesized via Microwave-Assisted Pyrolysis: A Potential Nanoprobe for Magneto-fluorescent Dual-Modality Bioimaging

Heteroatom-doped carbon dots (C-dots) have captured widespread research interest owing to high fluorescence and biocompatibility for multimodal bioimaging applications. Here, we exemplify a rapid, facile synthesis of ethylenediamine (EDA)-functionalized transition metal ion (Mn 2+, Fe 2+, Co 2+, and Ni 2+ )-doped C-dots via one-pot microwave (MW)-assisted pyrolysis at 800 W within 6 min using Citrus limon (lemon) extract as a carbon source. During MW pyrolysis, the precursor extract undergoes simultaneous carbonization and doping of metal ions onto C-dot surfaces in the presence of EDA. The EDA-functionalized transition metal ion-doped C-dots (i.e., Mn/C, Fe/C, Co/C, and Ni/C-dots) are collectively termed as TMCDs. The water-soluble TMCDs exhibited a size of 3.2 ± 0.485 nm and were enriched with amino and oxo functionalities and corresponding metal-oxide traces on the surfaces, as revealed from Fourier transfer infrared and X-ray photoelectron spectroscopy analyses. Interestingly, TMCDs demonstrated excitation-wavelength-dependent emission with brighter photoluminescence (PL) at 460 nm. Compared to pristine C-dots with a PL quantum yield (QY) of 48.31% and a fluorescence lifetime of 3.6 ns, the synthesized Mn/C, Fe/C, Co/C, and Ni/C-dots exhibited PL QY values of 35.71, 41.72, 75.07, and 50.84% as well as enhanced fluorescence lifetimes (τ av ) of 9.4, 8.6, 9.2, and 8.9 ns, respectively. The TMCDs significantly exhibited enhanced biocompatibility in human colon cancer cells (SW480) for fluorescence bioimaging and showed ferromagnetic and superparamagnetic behavior with vibrant T 1 -contrast ability. Interestingly, the maximum longitudinal ( r 1 ) relaxivity of 0.341 mM –1 s –1 was observed for Mn/C-dots in comparison to that of 3.1–3.5 mM –1 s –1 of clinically used Gd-DTPA magnetic resonance (MR)-contrast agent in vitro (1.5 T). Similarly, the maximum longitudinal relaxivity ( r 1 ) of 0.356 mM –1 s –1 was observed for Ni/C-dots (1.5 T) with respect to 4.16 ± 0.02 mM –1 s –1 attained for Gd-DTPA in vivo (8.45 T). Thus, the rapid, energy-efficient MW-assisted pyrolysis presents lemon extract derived, EDA-functionalized TMCDs with enhanced PL and efficient T 1 contrast as potential magneto-fluorescent nanoprobes for dual-modality bioimaging applications.