InGaN/GaN disk-in-nanowire white light emitting diodes on (001) silicon

This is the authors' abstract. We don't add key points for this paper.

High density (∼1011 cm−2) GaN nanowires and InGaN/GaN disk-in-nanowire heterostructures have been grown on (001) silicon substrates by plasma-assisted molecular beam epitaxy. The nanowires exhibit excellent uniformity in length and diameter and a broad emission is obtained by incorporating InGaN disks of varying composition along the length of the nanowires. Monolithic lighting emitting diodes were fabricated with appropriate n- and p-doping of contact layers. White light emission with chromaticity coordinates of x=0.29 and y=0.37 and a correlated color temperature of 5500–6500 K at an injection current of 50 A/cm2 is measured. The measured external quantum efficiency of the devices do not exhibit any rollover (droop) up to an injection current density of 400 A/cm2.