Low-temperature synthesis of MnxMg1−xFe2O4(x= 0–1) nanoparticles: cation distribution, structural and magnetic properties

Nanoferrites having composition Mn x Mg 1− x Fe 2 O 4 ( x = 0.0, 0.2, 0.4, 0.6, 0.8, 1.0) are synthesized by a low-temperature combustion method. The particle size measured from transmission electron microscopy and x-ray diffraction (XRD) patterns confirms the nanosized dimension of the as-prepared powder. From the analysis of XRD data with Scherrer's formula, the average crystallite size ranges from 23 to 33 nm and the lattice parameter ranges from 8.385 to 8.468 Å. Substitution of Mn 2+ in MgFe 2 O 4 causes an increase in the lattice constant, and this moderately distorts the lattice. Magnetic properties such as magnetization ( M s ), coercivity ( H c ) and remanence ( M r ) with increasing Mn 2+ concentration are studied at room temperature by a vibrating sample magnetometer. Substitution of Mn 2+ for Mg 2+ increases M s from 34.5 to 54.5 emu g −1 and decreases H c from 51.0 to 45.0 Oe. The results imply that the low-temperature combustion method is an efficient route for synthesis of nanoferrites without any extra calcination step. The as-prepared Mg–Mn ferrites are suitable for memory and switching circuits in digital computers.