Optical properties of multi-stacked InGaAs/GaNAs quantum dot solar cell fabricated on GaAs (311)B substrate

Quantum dot solar cells (QDSCs) comprised of 10 stacked pairs of strain-compensated InGaAs/GaNAs QD structure have been fabricated by atomic hydrogen-assisted molecular beam epitaxy. A homogeneous and high-density QD array structure with improved in-plane ordering and total density of ∼1012 cm−2 has been achieved on GaAs (311)B grown at 460 °C after stacking. The external quantum efficiency (EQE) of InGaAs/GaNAs QDSC increases in the longer wavelength range due to additive contribution from QD layers inserted in the intrinsic region. The short-circuit current density measured for QDSC is 17.2 mA/cm2 compared to 14.8 mA/cm2 of GaAs reference cell. Further, an increase in EQE due to photocurrent production by 2-step photon absorption has been observed at room temperature though it is still small at around 0.1%.