WO3/CeO2 Nanocomposite Powders: Synthesis, Characterization, and Reactivity

WO 3 /CeO 2 nanocomposite powders, characterized by increasing W/Ce atomic ratio, were prepared by depositing, by wet impregnation, different amounts of WO 3 on the CeO 2 surface. The powders were characterized by means of X-ray photoelectron and diffuse reflectance infrared Fourier transform spectroscopic techniques as well as thermal analysis. The WO 3 /CeO 2 samples are slightly reduced with respect to the pure oxides: the presence of W(V) and Ce(III), in addition to W(VI) and Ce(IV), is evident at the interface supported/supporting oxides. Interesting information concerning particle dimensions and growth mode derive by X-ray diffraction and transmission electron microscopy. New acidic/basic and redox sites are evident on the surface of the WO 3 /CeO 2 nanocomposites. The interaction with methanol was also investigated. Methanol interacts both molecularly and dissociatively with the WO 3 /CeO 2 surface; the dissociation is prevalent on the sample characterized by a lower content of WO 3, whereas a mainly molecular interaction is observed with increasing amount of tungsten oxide. Oxidation of methanol is evident from T ≥ 423 K on the sample with [W/Ce] nominal = 0.025 and from T ≥ 473 K on the one richer in WO 3 . The reactivity toward methanol oxidation is higher in the sample with a lower content of WO 3, but the sample richer in WO 3 shows a higher selectivity with respect to formation of carbon dioxide.