) beginning at 55 °C, leading to their flowing at temperatures above 130 °C, as determined by dynamic mechanical analysis, with E' below 1 MPa and tan δ above 1. Their structure was evaluated by wide angle X-ray scattering and NMR analysis was used to evaluate the API-IL stability after thermomechanical processing. Release experiments performed under simulated physiological conditions on filaments evidenced a release of 85% after 7 days immersion. These results demonstrate the advantage of using an API-IL as plasticizer of a resorbable biopolymer. The resulting material can be shaped by a continuous thermomechanical process and used as a drug delivery system.