Synthesis and properties of sulfonated polyimides derived from bis(sulfophenoxy) benzidines

A series of aromatic sulfonated polyimides (SPIs) bearing sulfophenoxy side groups have been successfully synthesized and evaluated as polymer electrolyte membranes for fuel cell applications. The SPIs had high viscosity and gave tough and flexible membranes. The SPI membranes showed anisotropic membrane swelling in water with much larger dimensional change in thickness direction than in plane one. They showed the better proton‐conducting performance even in the lower relative humidity (RH) range than the other SPI membranes, for example, a high proton conductivity of 0.05 S/cm at 50 % RH and 120 °C. They maintained high mechanical strength and conductivity after aging in water at 130 °C for 500 h, showing much better water stability compared with the main‐chain‐type SPI and side‐chain‐type SPI membranes reported so far. In polymer electrolyte fuel cells (PEFCs) operated at 90 °C and 84–30%RH, they showed fairly high cell performances and have high potential for PEFC applications.